以苯并噁嗪(BZ)作为氰酸酯(CE)-环氧树脂(EP)-双马来酰亚胺(BMI)基胶粘剂的改性剂,探讨了BZ含量对改性胶粘剂的力学性能、介电性能、耐热性、耐水性和可操作性等影响。结果表明:当w(BZ)=2%时,改性胶粘剂的综合性能较好,其常温剪切强度(24.98 MPa)和高温(200℃)剪切强度(21.24 MPa)分别比未改性胶粘剂提高了16.9%和32.7%、介电系数低于3.0、吸水25 h后的吸水率仍低于1.2%且耐热性能未受到影响;170℃时凝胶时间为71 min,说明改性胶粘剂的可操作性较强,并且满足使用期的要求;改性胶粘剂在电子电器行业中具有良好的应用前景。
Abstract：With benzoxazine(BZ) as modifier of CE-EP-BMI(cyanate ester-epoxy resin-bismaleimide) base adhesive,the influences of BZ contents were discussed on mechanics properties,dielectric properties,heat resistance,water resistance and maneuverability of modified adhesive.The result showed that the modified adhesive had better combination property because the shear strength(24.98 MPa) at room temperature and shear strength(21.24 MPa) at high temperature(200 ℃) of modified adhesive were 16.9% and 32.7% more than those of unmodified adhesive,dielectric coefficient was less than 3.0,water absorption after 25 h in boiling water was still less than 1.2%,and heat resistance was not affected when mass fraction of BZ was 2%.The modified adhesive had better maneuverability and could meet requirements of applicable period because its gelation time at 170 ℃ was 71 min.The modified adhesive had good application prospect in electrical and electronic equipment industry.
[1]Laskoski M,Dominguez D D,Keller T M.Synthesis andproperties of a liquid oligomeric cyanate ester resin[J].Polymer,2006,47(11):3 727-3 733.
[2]Zhang B F,Wang Z G,Zhang X.Synthesis and properties ofa series of cyanate resins based on phenolphthalein and itsderivatives[J].Polymer,2009,50(3):817-824.
[3]Lin R H,Lu W H,Lin C W.Cure reactions in the blend ofcyanate ester with maleimide[J].Polymer,2004,45(13):4 423-4 435.
[4]Mondrago I,Solar L,Nohales A,et al.Properties andstructure of cyanate ester/polysulfone/organoclay nano-composites[J].Polymer,2006,47(10):3 401-3 409.
[5]李文峰,王国建.DF-3740韧性氰酸酯/双马来酰亚树脂的性能[J].材料工程,2008(增刊1):395-397,401.
[6]方芬,颜红侠,李倩,等.BMI/BCE树脂体系反应固化动力学研究[J].应用化学,2007,24(3):291-295.
[7]李俊燕,陈平,马泽民,等.酚酞基聚醚酮/环氧树脂/氰酸酯半互穿聚合物的制备及性能[J].高分子材料与工程,2009,25(7):141-143.
[8]Prokopec R,Humer K,Maix R K,et al.Characterization ofadvanced cyanate ester/epoxy insulation systems beforeand after reactor irradiation[J].Fusion Engineering andDesign,2010,85(2):227-233.
[9]谢文峰,李俊菊,黄志雄.双马来酰亚胺与环氧改性氰酸酯固化工艺研究[J].武汉理工大学学报,2007,29(2):16-19.
[10]李俊菊.氰酸酯/双马/环氧共聚改性及其复合材料性能研究[D].湖北:武汉理工大学出版社,2006:1-53.
[11]李玲,陈剑楠.BMI改性苯并恶嗪树脂及其复合材料研究[J].工程塑料应用,2009,37(6):20-23.
[12]Ejfler J,Krauzy-Dziedzic K,Szafert S,et al.Novel chiraland achiral benzoxazine monomers and their thermal poly-merization[J].Macromolecules,2009,42(12):4 008-4 015.
[13]Agag T,Arza C R,Maurer F H J,et al.primary amine-functional benzoxazine monomers and their use for amide-containing monomeric benzoxazines[J].Macromolecules,2010,43(6):2 748-2 758.
[14]白会超,王继辉,冀运东.耐高温苯并恶嗪的合成与表征[J].宇航材料工艺,2008,38(3):45-48.
[15]凌鸿,顾宜,谢美丽.F级苯并噁嗪树脂基玻璃布层压板的研制[J].绝缘材料,2001,34(1):20-23.
[16]王丁,程斌,刘峰,等.有机硅改性酚醛环氧树脂耐高温胶粘剂的研制[J].中国胶粘剂,2007,16(3):23-27.
基本信息:
DOI：10.13416/j.ca.2011.11.014
中图分类号:TQ433.43
引用信息:
[1]杨满红,张教强,季铁正,等.氰酸酯环氧双马来酰亚胺基胶粘剂的苯并噁嗪改性研究[J].中国胶粘剂,2011,20(11):34-37.DOI:10.13416/j.ca.2011.11.014.
2011-11-30
2011-11-30