以2-乙基己基丙烯酸酯(2-EHA)、丙烯酸(AA)、丙烯酸丁酯(BA)为原料,2′-羟基-4′,5′-二甲基乙酰苯(HP-8)为光引发剂,通过紫外光引发聚合的方法制备出一系列丙烯酸酯预聚物,并通过UV-DSC和RT-FTIR,探究较佳光聚合体系。以上述丙烯酸酯预聚物为基体,通过加入不同含量的交联剂,制备出一系列半互穿网络结构的UV固化丙烯酸酯压敏胶(PSA),系统地研究了UV辐射能和乙氧基化三羟甲基丙烷三丙烯酸酯(ETPTA)含量对UV固化丙烯酸酯PSA的凝胶含量、粘接性能和黏弹性性能影响规律。研究结果表明:较佳光引发剂含量为0.5%,较佳UV辐射能为600 mJ/cm2,且当以PI-0.50为预聚物体系时,UV固化丙烯酸酯PSA的综合性能优异。此外,当ETPTA添加量为6%时,UV固化丙烯酸酯PSA的剪切破坏温度高达200℃。
Abstract：Using 2-ethylhexyl acrylate(2-EHA),acrylic acid(AA),and butyl acrylate(BA) as raw materials,2′-hydroxy-4′,5′-dimethylacetophenone(HP-8)as photoinitiator,a series of acrylic pre-polymers were synthesized by UV light initiation polymerization,and then the polymerization system was studied by UV-DSC and RT-FTIR. A series of semi interpenetrating network structure of UV-cured acrylate pressure sensitive adhesive(PSA)was prepared by adding different contents of crosslinking agent. The effects of UV radiation and ethoxylated trimethyol propane triacrylate(ETPTA)content on the gel content,adhesion and viscoelastic properties of UV-cured acrylate PSA were systematically studied. The research results showed that the appropriate content of photoinitiator was 0.5%,the appropriate UV radiation energy was 600 mJ/cm2,and when PI-0.50 was used as prepolymer system,the comprehensive properties of UV-cured acrylate PSA was excellent. In addition,when the addition of ETPTA was 6%,the shear failure temperature of UV-cured acrylate PSA was as high as 200 ℃.
[1] DASTJERDI Z,CRANSTON E D,DUBéM A. Pressure sensitive adhesive property modification using cellulose nanocrystals[J]. International Journal of Adhesion and Adhesives,2018,81:36-42.
[2] JIN K,BARREIRO D L,MARTIN-MARTINEZ F J,et al.Improving the performance of pressure sensitive adhesives by tuning the crosslinking density and locations[J].Polymer,2018,154:164-171.
[3] FELDSTEIN M M,DORMIDONTOVA E E,KHOKHLOV A R.Pressure sensitive adhesives based on interpolymer complexes[J]. Progress in Polymer Science,2015,42:79-153.
[4] CZECH Z,LOCLAIR H,WESOLOWSKA M.Photoreactivity adjustment of acrylic PSA[J].Reviews on Advanced Materials Science,2007,14(2):141-150.
[5] SANGERMANO M,RAZZA N,CRIVELLO J V. Cationic UV-curing:Technology and applications[J]. Macromolecular Materials and Engineering,2014,299(7):775-793.
[6] LIAN Q,LI Y,SAYYED A A S,et al. Facile strategy in designing epoxy/paraffin multiple phase change materials for thermal energy storage applications[J].ACS Sustainable Chemistry&Engineering,2018,6(3):3375-3384.
[7] LI Y,LIAN Q,LIN Z,et al. Epoxy/polysiloxane intimate intermixing networks driven by intrinsic motive force to achieve ultralow-temperature damping properties[J].Journal of Materials Chemistry A,2017,5(33):17549-17562.
[8]贺贝贝，解一军.紫外光本体聚合制备丙烯酸酯压敏胶[J].化工进展，2017,36(12):4508-4512.
[9]黄海洲，房成，林中祥.UV固化无溶剂型丙烯酸酯压敏胶的合成与性能表征[J].精细化工，2016,33(12):1428-1433.
[10] CZECH Z,BUTWIN A,KABATC J. Photoreactive UVcrosslinkable acrylic pressure-sensitive adhesives containing type-II photoinitiators[J].European Polymer Journal,2011,47(2):225-229.
[11] SHIM G S,KIM J S,BACK J H,et al.Preparation of acrylic pressure-sensitive adhesives by UV/UV step curing as a way of lifting the limitations of conventional dual curing techniques[J].InternationalJournalofAdhesionandAdhesives,2020,96(1):102445.
[12] ALAM R,KHAN M A,KHAN R A,et al. Study on the physico-mechanical properties of photo-cured chitosan films with oligomer and acrylate monomer[J]. Journal of Polymers and the Environment,2008,16(3):213-219.
[13] NASON C,ROPER T,HOYLE C,et al. UV-Induced frontal polymerization of multifunctional(meth)acrylates[J].Macromolecules,2005,38(13):5506-5512.
[14] CORCIONE C E,MALUCELLI G,FRIGIONE M,et. al.UV-curable epoxy systems containing hyperbranched polymers:Kinetics investigation by photo-DSC and realtime FT-IR experiments[J].Polymer Testing,2009,28(2):157-164.
[15] LECAMP L,YOUSSEF B,BUNEL C,et al.Photoinitiated polymerization of a dimethacrylate oligomer:1.Influence of photoinitiator concentration, temperature and light intensity[J].Polymer,1997,38(25):6089-6096.
[16] DECKER C,KELLER L,ZAHOUILY K,et al.Synthesis of nanocomposite polymers by UV-radiation curing[J].Polymer,2005,46(17):6640-6648.
[17] EBE K,SENO H,HORIGOME K. UV curable pressuresensitive adhesives for fabricating semiconductors. I.Development of easily peelable dicing tapes[J].Journal of Applied Polymer Science,2003,90(2):436-441.
[18] AGIRRE A,HERAS-ALARCON?C,WANG T,et al.Waterborne,semicrystalline,pressure-sensitive adhesives with temperature-responsiveness and optimum properties[J].ACS Applied Materials&Interfaces,2010,2(2):443-451.
[19] SASAKI H. Photocurable pressure-sensitive adhesives using alkyl oxetane[J].Journal of Photopolymer Science&Technology,2003,14(2):296-305.
[20] FALSAFI A,TIRRELL M,POCIUS A V. Compositional effects on the adhesion of acrylic pressure sensitive adhesives[J].Langmuir,2000,16(4):1816-1824.
[21]湛露.UV固化型丙烯酸酯压敏胶的制备与性能研究[D].武汉：湖北大学，2013.
[22]魏弘利.UV固化型光学透明压敏胶膜的制备及性能研究[D].西安：西安电子科技大学，2016.
[23]王艳.紫外光引发聚合法制备光固化丙烯酸酯压敏胶的研究[D].天津：河北工业大学，2014.
[24]刘明珠，李磊，毛胜华，等.超低剥离强度溶剂型丙烯酸酯压敏胶性能研究[J].中国胶粘剂，2018,27(10):
[25] 4鲁3-道46欢.，王斌，黄月文.耐高温丙烯酸酯类压敏胶的研究进展[J].化工进展，2019,38(5):210-216.
[26] LI Y,CHENG J,ZHANG J. A newly designed dualfunctional epoxy monomer for preparation of fishboneshaped heterochain polymer with a high damping property at low temperature[J]. Macromolecular Materials and Engineering,2017,302(5):1600574.
基本信息:
DOI：10.13416/j.ca.2020.01.003
中图分类号:TQ436.3
引用信息:
[1]李言,廉青松,张博等.UV固化无溶剂型耐高温丙烯酸酯压敏胶的研制及性能研究[J].中国胶粘剂,2020,29(01):9-15+26.DOI:10.13416/j.ca.2020.01.003.
基金信息: