以多苯基多亚甲基多异氰酸酯(PAPI)和硅氢封端有机硅树脂(PDMS)为主要原料,制备了一种可在室温下固化的含碳硼烷耐高低温胶粘剂用树脂。通过差示扫描量热法(DSC)研究其固化反应中的各个固化特征,并且分别采用了Kissinger法和Ozawa法计算该反应的反应活化能、反应级数和频率因子等动力学参数。研究结果表明:由两种方法计算所得的表观活化能分别为32.9和36.9 kJ/mol,固化反应级数分别为0.86和0.95,接近一级反应。
Abstract:Using polyaryl polymethylene polyisocyanate(PAPI)and silicon hydrogen-terminated silicone resin(PDMS)as the main raw materials,a kind of high and low temperature resistant adhesive resin containing carborane,which could be cured at room temperature,was prepared. Differential scanning calorimetry(DSC)was used to study the curing characteristics of the reaction,and the reaction activation energy,reaction order,frequency factor and other kinetic parameters were calculated by Kissinger and Ozawa method,respectively. The research results showed that the apparent activation energy calculated by two methods was 32.9 and 36.9 kJ/mol,and the curing reaction order was 0.86 and 0.95,respectively,which were close to the first order reaction.
[1]段雪蕾.用于PVC粘接的双组份聚氨酯胶粘剂合成的研究[D].西安:西安科技大学,2012.
[2]李国遵,高之香,李士学,等.聚氨酯胶粘剂的研究进展、合成、改性与应用[J].粘接,2019,40(5):177-180.
[3]陈珊,赵娟,陈功,等.碳硼烷聚酯及其改性聚氨酯胶黏剂的合成及性能研究[J].高分子学报,2011(12):1368-1373.
[4]吴攀洛,张思思,李文翔,等.异佛尔酮二胺/环氧树脂非等温固化动力学研究[J].胶体与聚合物,2018,36(2):69-71.
[5]方建波,顾浩.用差示扫描量热法研究环氧树脂-咪唑改性双氰胺离子液体体系[J].化学世界,2017,58(12):705-709.
[6]李艳春.热分析动力学在含能材料中的应用[D].南京:南京理工大学,2010.
基本信息:
DOI:10.13416/j.ca.2020.05.002
中图分类号:TQ433.432
引用信息:
[1]许星烨,周权,宋宁等.聚氨酯胶粘剂的固化反应及动力学研究[J].中国胶粘剂,2020,29(05):1-5.DOI:10.13416/j.ca.2020.05.002.
基金信息:
装备预研领域基金(61409220409)