NaOH与NaClO改性淀粉胶粘剂的流变性能研究
基金项目(Foundation): 国家重大科研仪器研制项目(51927810); 湖南省教育厅优秀青年项目(18B288)
邮箱(Email): lixianggang@hut.edu.cn;
DOI: 10.13416/j.ca.2022.05.004
摘要:

以NaOH为糊化剂、NaClO为氧化剂,对淀粉进行了糊化氧化改性,并以此为基础制备了淀粉胶粘剂。采用流变学的表征方法系统地研究了温度、NaOH与NaClO用量对于淀粉糊化过程的影响,并探究了NaOH与NaClO用量对淀粉胶粘剂性能的影响。研究结果表明:玉米淀粉的糊化温度为60~70℃,当加入NaOH为糊化剂时,室温之下淀粉已经开始部分糊化。以NaClO为氧化剂对淀粉进行改性时,随着NaClO用量的增加,改性淀粉的黏度降低,流动性明显变好,从半凝胶变为可流动的液体。由淀粉胶粘剂的流变测试可得,淀粉胶粘剂随角频率的增加,复数黏度呈幂律降低,表现出剪切变稀的现象。一定量NaOH和NaClO加入降低了淀粉胶粘剂的储能模量、损耗模量和复数黏度。添加质量分数为10%(相对于干淀粉质量而言)NaOH溶液和20%(相对于干淀粉质量而言)NaClO溶液制备的淀粉胶粘剂的效果更佳。

Abstract:

Starch was modified by gelatinization and oxidation with NaOH as gelatinization agent and NaClO as oxidant,and starch adhesive was prepared on this basis. The effects of temperature,the amount of NaOH and NaClO on the gelatinization process of starch were systematically studied by rheological characterization method,and the effects of the amount of NaOH and NaClO on the properties of starch adhesive were also explored. The research results showed that the gelatinization temperature of corn starch was 60-70 ℃. When NaOH was added as gelatinization agent,the starch had begun to partially gelatinize at room temperature. When starch was modified with NaClO as oxidant,with the increase of NaClO amount,the viscosity of modified starch decreased,the fluidity improved obviously,and the semi-gel changed into the flowing liquid. From the rheological test of starch adhesive,it could be seen that with the increase of angular frequency,the complex viscosity of starch adhesive decreased in a power-law manner,which showed the phenomenon of shear thinning. The addition of a certain amount of NaOH and NaClO reduced the storage modulus,loss modulus and complex viscosity of starch adhesive. The effects of starch adhesive prepared by adding 10%(relative to the mass of dry starch)NaOH solution and 20%(relative to the mass of dry starch)NaClO solution were relatively better.

参考文献

[1]张云飞,刘辉,吴艳光,等.酚醛树脂改性脲醛树脂胶粘剂的研究进展[J].武汉工程大学学报,2015(4):23-28.

[2]李娜.橡实淀粉胶粘剂的制备工艺研究[D].河南:郑州大学,2016.

[3]乔治邦.淀粉基木材胶粘剂的制备及性能研究[D].黑龙江:东北林业大学,2015.

[4]何泽森,孙瑾,樊奇,等.我国淀粉基木材胶粘剂的研究与应用[J].木材工业,2017,31(1):32-36.

[5]阚雨村,陈复生,刘伯业.淀粉基胶粘剂改性及应用的研究进展[J].中国胶粘剂,2019,28(10):55-60.

[6]王玉忠,汪秀丽,宋飞.淀粉基新材料[M].北京:化学工业出版社,2015.

[7]王静.基于非对称场流分离多检测联用技术研究淀粉退化行为[D].保定:河北大学,2018.

[8]司红岩.玉米淀粉胶粘剂的研究[D].河南:郑州大学,2015.

[9] LAI L N,KARIM A A,NORZIAH M H,et al. Effects of Na2CO3and NaOH on pasting properties of selected native cereal starches[J].Journal of Food Science,2004,69(4):249-256.

[10] GARRIDO L H,SCHNITZLER E,ZORTéA M E B,et al.Physicochemical properties of cassava starch oxidized by sodium hypochlorite[J]. Journal of Food Science and Technology,2014,51(10):2640-2647.

[11] ZHANG Y R,WANG X L,ZHAO G M,et al.Preparation and properties of oxidized starch with high degree of oxidation[J].Carbohydrate Polymers,2012,87(4):2554-2562.

[12] KUAKPETOON D,WANG Y J. Structural characteristics and physicochemical properties of oxidized corn starches varying in amylose content[J]. Carbohydrate Research,2006,341(11):1896-1915.

[13]杨贞.碱性条件下魔芋胶对小麦淀粉凝胶流变和质构特性的影响[D].郑州:河南农业大学,2018.

[14]肖俊.双氧水氧化玉米淀粉的干法制备及应用[D].无锡:江南大学,2008.

[15] ZHAO X F,PENG L Q,WANG H L,et al.Environmentfriendly urea-oxidized starch adhesive with zero formaldehyde-emission[J]. Carbohydrate Polymers,2017,181:1112.

基本信息:

DOI:10.13416/j.ca.2022.05.004

中图分类号:TQ432.2

引用信息:

[1]阳志强,李辉,李祥刚.NaOH与NaClO改性淀粉胶粘剂的流变性能研究[J].中国胶粘剂,2022,31(05):24-31+37.DOI:10.13416/j.ca.2022.05.004.

基金信息:

国家重大科研仪器研制项目(51927810); 湖南省教育厅优秀青年项目(18B288)

引用

GB/T 7714-2015 格式引文
MLA格式引文
APA格式引文